Materials having non-linear electrical resistance characteristics

ABSTRACT

A polymer composition containing silicon carbide of a critical maximum average particle size can be processed into heat-shrinkable articles possessing nonlinear electrical resistance characteristics. An embodiment of the invention provides a heat-shrinkable article comprising a laminate of a layer of elastomer, including silicon carbide particles, and a layer of a heat-shrinkable polymeric material. The elastomeric layer may be a blend of a rubbery polymer and a low density polyethylene having dispersed therein particulate silicon carbide of particle size finer than about 300 grit.

This is a division of application Ser. No. 393,509, filed Aug. 31, 1973, now U.S. Pat. No. 3,950,604.

BACKGROUND OF THE INVENTION

This invention relates to materials having nonlinear electrical resistance characteristics.

In the past, in order to suppress the occurrence of electrical discharges on surfaces of high-voltage cable insulation, for example at high-voltage cable terminations, the insulation was provided with a stress control covering of a material having nonlinear electrical resistance characteristics. Prior art coverings were typically in the form of preformed sleeves, wrapped tapes or dried coatings of such materials. These coverings have the disadvantage that, in general, an effective stress control covering can be obtained only by careful and skillful application of the covering, that the materials have undesirable properties, for example rapid aging, at elevated temperatures, or that the elongation properties of the materials are inadequate which may result in the covering cracking if the cable expands, as it will do if heat cycling occurs, or is bent or twisted.

It has been proposed to form a stress control covering on cable insulation by heat-shrinking a heat-shrinkable tube of a material loaded with silicon carbide onto the insulation. Such tubes would have the advantage that they could be easily installed, that no skill would be required in maintaining correct tension of the covering and that a predetermined thickness of covering could be guaranteed. To achieve the necessary nonlinearity of resistance, the volume loading of silicon carbide in the material needs to be in the region of 40%. At such loadings, heretofore known materials capable of being rendered heat-shrinkable have extremely poor physical properties, such as insufficient elongation at break and poor tear strength. Thus they break or tear when attempts are made to process them into heat-shrinkable articles.

SUMMARY OF THE INVENTION

It is therefore an object of this invention to provide a composition of matter having nonlinear electrical resistance.

It is another object of this invention to provide a heat-shrinkable article having nonlinear electrical resistance.

BRIEF DESCRIPTION OF THE DRAWINGS

The invention both as to its organization and principles of operation, together with further objects and advantages thereof, may better be understood by referring to the following detailed description of embodiments of the invention when taken in conjunction with the accompanying drawings in which:

FIG. 1 illustrates, in cross-section, a heat-shrinkable laminate according to the invention.

FIG. 1A illustrates, in partial cross-sectional end view, a heat shrinkable tube according to the invention.

FIG. 1B illustrates, in partial cross-sectional end view, another heat-shrinkable tube according to the invention.

FIG. 2 illustrates a sectional side elevation of one end of a cable which has been prepared for termination in accordance with this invention.

FIG. 3 illustrates circuitary and apparatus for determining discharge magnitude in accordance with this invention.

FIGS. 4, 5, 6 and 7 illustrate current voltage stress plots in accordance with this invention.

DESCRIPTION OF A PREFERRED EMBODIMENT

The present invention is based on the observation that certain polymer combinations containing silicon carbide of a critical maximum average particle size possess nonlinear electrical resistance characteristics and can be processed into heat-shrinkable articles.

According to the invention, there is provided a material which can be processed into heat-shrinkable articles, which material comprises a blend of

(a) an ethylene-propylene rubber copolymer or an ethylene-non-conjugated diene rubber terpolymer, wherein the ethylene content is at least 65%, preferably at least 70%; or a butadiene/acrylonitrile rubber containing 10% to 40% by weight acrylonitrile,

(b) a copolymer of ethylene and a copolymerisable monomer preferably selected from the group consisting of methyl, ethyl and other lower alkyl-acrylates and methacrylates, vinyl acetate and lower alkyl esters of maleic, fumaric and itaconic acids, this component being optional when component (a) is a butadiene/acrylonitrile rubber, and

(c) a low density polyethylene, which blend has dispersed therein silicon carbide and, optionally, one or more conducting particulate fillers, the particle size of the silicon carbide being finer than 400 grit size, preferably finer than 500 grit size.

The blend preferably comprises, per 100 parts by weight of component (a), from 20 to 75, preferably from 25 to 50, parts by weight of component (b) and from 15 to 70, preferably from 20 to 50, parts by weight of component (c).

As component (a), there is preferably used an ethylene-propylene-non-conjugated diene terpolymer having a high molecular weight, for example one having a high Mooney viscosity, which may contain up to 40 percent by weight of a naphthenic oil as a processing aid. There is especially used one of those terpolymers listed in Tables 1 to 3 hereunder, which Tables give details of chemical compositions, Mooney viscosities and the nature and quantity of processing oil, if any, used. The code numbers are those allotted by the suppliers.

                                      TABLE 1                                      __________________________________________________________________________     Royalene                                                                       (Manufactured                                                                  by Uniroyal)                                                                           301T  400   512   521   611   Royalene                                                                               1812  1750                       __________________________________________________________________________     Ethylene                              Ethylene                                 Content %                                                                              65    65    68    68    70    Content %                                                                              77.0  77.0                       Mooney Viscos-                        Mooney Viscos-                           ity (250° F.)                  ity (250° F.)                     ML1 + 4 34-46 32-45 55-70 40-50 35-45 ML1 + 4 35-45 35-45                      Nature of                             Nature of                                Termonomer                                                                             D.C.P.                                                                               D.C.P.                                                                               E.N.B.                                                                               E.N.B.                                                                               E.N.B.                                                                               Termonomer                                                                             E.N.B.                                                                               E.N.B.                     Quantity of                           Quantity of                              Termonomer                                                                              2.5-3.5%                                                                             2.5-3.5%                                                                             2.5-3.5%                                                                             2.5-3.5%                                                                             2.5-3.5%                                                                            Termonomer                                                                              2.5-3.5%                                                                             2.5-3.5%                  Nature of     Naph-             Paraf-                                                                               Nature of                                Processing Oil                                                                         0     thenic                                                                               0     0     finic Processing Oil                                                                         0     0                          Quantity of                     Quantity of                                    Processing Oil                                                                         0     100%  0     0     40%   Processing Oil                                                                         0     0                          __________________________________________________________________________      1812 is identical to 611 but without the processing oil.                       1750 is an experimental grade of 611.                                    

                  TABLE 2                                                          ______________________________________                                         Nordel                                                                         (Manufactured                                                                  by Du Pont)                                                                               1145       1560       1500                                          ______________________________________                                         Ethylene                                                                       Content     65%        72%        72%                                          Mooney                Too high   Too high                                      Viscosity                                                                      (250° F.)                                                                          45         to measure to measure                                    Nature of                                                                      Termonomer 1,4-hexadiene                                                                             1,4-hexadiene                                                                             1,4-hexadiene                                 Quantity of                                                                    Termonomer 2.6%       3.0%       3.0%                                          Nature of                                                                      Processing Oil                                                                            0          0          0                                             Quantity of                                                                    Processing Oil                                                                            0          0          0                                             ______________________________________                                          Nordel 1560 is a nonmilling grade.                                             Nordel 1500 is identical to 1560 but supplied as grains.                 

                  TABLE 3                                                          ______________________________________                                         Montecantini                                                                               535D              038DMX                                           ______________________________________                                         Ethylene                                                                       Content     69%                57-70%                                          Mooney                                                                         Viscosity                                                                      212° F.                                                                             50-60             75-85                                            Nature of                                                                      Termonomer  D.C.P.            E.N.B.                                           Quantity of                                                                    Termonomer   4%               3.5%                                             Nature of                                                                      Processing Oil                                                                             Naphthenic non staining                                                                          0                                                Quantity of                                                                    Processing Oil                                                                             50%               0                                                ______________________________________                                          In the above Tables, D.C.P. stands for dicyclopentadiene and E.N.B. stand      for ethylidene norbornene.                                               

It has also been found that various grades of Keltans (manufactured by Dutch State Mines) and Intolans (manufactured by International Synthetic Rubber Co.) are suitable ethylene-propylene rubbers, provided the ethylene proportion is sufficiently high. Details of the probable chemical composition of many ethylene-propylene rubbers are given in an article entitled "Polyolefin Elastomers Based on Ethylene and Propylene" by F. P. Baldwin and G. Ver Strate, in Rubber Chemistry and Technology, Volume 45, No. 3, Apr. 30, 1972, Pages 709 to 881.

It has also been found that nitrile rubbers may be especially mentioned, for example, Breon 1041.

As component (b), there is preferably used an ethylene-ethyl acrylate copolymer containing about 18% by weight of ethyl acrylate.

Suitable silicon carbides are, for example, those manufactured by the Carborundum Company and known as F500, F600, 800, 1000, 1200, 1500 and especially F1200/S, and those manufactured by A/S Arendal Smetherverk, Eydehaven, Norway and known as F500/13, F600/9, F800/7, F1,000/5 and F1200/3. These silicon carbides have an average particle size of less than 15 microns, all of the particles having a particle size of less than 45 microns. In general, the smaller the average particle size of the silicon carbide, the better the physical properties of the material as regards processing into heat-shrinkable articles. The silicon carbide may be substantially pure or may contain impurities, such as aluminium, boron, titanium and/or zirconium, which modify its electrical conductivity.

As the conducting particulate filler, there may be used, for example, carbon black and/or a finely divided metal, for example zinc, aluminium, chromium, copper, bronze, brass, iron, lead, silver or nickel. For practical purposes, including cost, finely divided aluminium, copper, bronze, brass or iron is preferably used as the metal. The use of carbon black has the advantages that it reinforces the polymer base and that the amount of silicon carbide necessary is reduced which results in the material having more favorable properties, for example a better expansion ratio. Finely divided metals do not reinforce the polymer base as well as carbon black does, but do permit the use of smaller amounts of silicon carbide.

The present invention also provides an article, for example a tube, which can be rendered heat-shrinkable, formed of the material specified above. Such articles may be formed by conventional methods, for example by extrusion.

The present invention also provides a heat-shrinkable article, for example a tube, of the material specified above. By the term "heat-shrinkable article", it is meant an article which retains its dimensions under low or normal temperature conditions but at least one dimension of which is reduced upon heating to a critical temperature.

The article which can be rendered heat-shrinkable can be so rendered by normal methods. Thus, the material of construction is firstly cross-linked, for example by irradiation with β- or γ-radiation, the article is then expanded by the desired amount at a temperature at or above said critical temperature while maintaining it in the expanded state. The material of construction may be cross-linked prior to processing it into an article. Of course, when the material is to be chemically cross-linked, the cross-linked agent, for example a peroxide, must be incorporated during the manufacture of the material. It has been found that the method of cross-linking has a marked effect on the amount of elongation at break of the material and, therefore, on the degree of heat-shrinkable properties that can be imparted to the material. Thus, it has been found that, for a given material, an expansion ratio (determined from the change on expansion in internal diameter of a hollow article of the material) greater than 1.8:1 cannot be obtained if cross-linking has been effected by irradiation with β- or γ-radiation; whereas, an expansion ratio of up to 3.0:1 can be obtained if cross-linking has been effected chemically using a peroxide.

The material of the invention may contain additional ingredients, for example other fillers, stabilizers anti-oxidants, lubricants or cure systems, for example polyunsaturated monomers or peroxides.

The heat-shrinkable articles of the invention may be heat-shrunk onto, for example, cable terminations to provide stress control coverings thereon. It will be appreciated, however, that they have applications to electrical parts other than cable terminations where it is desirable to have stress control coverings, for example, to lighting arrestors, switch components or ends of stator bars.

According to a modification of the invention, there is provided an article, which can be rendered heat-shrinkable, which article comprises a laminate of a layer of an elastomer having dispersed therein silicon carbide and, optionally, a particular filler, and a layer of a polymeric material, which polymeric material can be rendered heat-shrinkable.

As the elastomer, there may be used, for example one of the rubbers mentioned above, a fluoroelastomer, a chlorinated or chlorosulphonated polyethylene, a polyurethane, an acrylate, a silicone or a fluorosilicone.

There is also provided a heat-shrinkable article illustrated in FIG. 1, comprising a laminate 20 of a layer 21 of an elastomer having dispersed therein silicon carbide and a layer 22 of a heat-shrinkable polymeric material.

The grade of the silicon carbide is preferably the same as that mentioned above, but coarser grades, for example grades as coarse as 300 grit size, may be used.

The elastomer layer 21 may be inside or outside the layer of polymeric material as illustrated with reference to a heat-shrinkable tube member 23 in FIGS. 1A and 1B respectively. It is preferable, however, for the elastomer layer 21 to be on the inside as in FIG. 1A so that an insulating layer of polymeric material is on top, whereby better stress grading on, for example, cable terminations is obtained since at high stress points all of the conducting particles are coated with the insulating layer of polymeric material and sharp grains of silicon carbide cannot initiate discharges.

Heat-shrinkable articles according to the modification of the invention may be obtained in the normal manner, for example as described above, and have similar applications to the article described earlier in this specification.

The laminar articles of the modification of the invention have two main advantages over the articles described earlier, namely that they can have higher expansion ratios (determined from the change in internal diameter of the article on expansion), for example up to 5 or 6 to 1 and, depending on the elastomer, excellent oil resistance.

In the modification of the invention, it is also possible for the article to comprise a laminate of a layer of material comprising the above mentioned blend of polymers having dispersed therein silicon carbide and a layer of a polymeric material, but in such cases the expansion ratios would be limited.

The present invention also provides an electrical member, for example an electric cable, which has had shrunk thereabout a heat-shrinkable article of the invention.

The following examples illustrate embodiments of the invention;

EXAMPLE 1

The following substances were mixed together in a twin roll laboratory mill at about 120° C.:

    ______________________________________                                                                   Parts by                                             Substance                 Weight                                               ______________________________________                                         Royalene 611              100                                                  DYNH                      40                                                   DPD 6169                  45                                                   Agerite Resin D           5                                                    Silicon Carbide                                                                (Grade F1200/3 ex Carborundum Co.)                                                                       380                                                  Triallyl Cyanurate        2.5                                                  Zinc Stearate             1.8                                                  ______________________________________                                    

Royalene 611 is an ethylene-propylene-ethylidene norbornene terpolymer, containing approximately 70% of ethylene, about 3.5% ENB and having a Mooney Viscosity of about 40. It is oil extended with 40 phr paraffinic oil and is supplied by Uniroyal Limited.

Silicon Carbide (Grade F1200/3) is made by the Carborundum Co. The average particle size of this material is about 3 microns.

DYNH is a low density polyethylene. MFI 3 made by Union Carbide.

The nonlinear resistance of the resulting material was measured by the following method:

In accordance with BS 2782 Pt. 201C, a plaque of the material having a thickness of 1 mm was placed between two circular brass electrodes, one on each side of the plaque, and the current flowing across the plaque was measured at different applied DC voltages using a conventional testing apparatus in a manner well known in the art. For a given material I=KVγ

were

I=current

V=voltage

K is a constant and

γ is a constant (1 for a material which obeys Ohm's Law).

The current I was measured against the voltage V from 100 volts to 10 kilovolts. It was founded that the material did not obey Ohm's Law; the value for gamma being 5.1.

The material was then extruded into tubing having an internal diameter of 0.490 in. and a wall thickness of 0.090 in. The tubing was irradiated with high energy electrons at 1.5 MeV, to a dose of 12.5 Mrads, after which the following properties were determined:

    ______________________________________                                                   Tensile     Elongation 100%                                          Temperature                                                                              Strength    at Break   Modulus                                       ______________________________________                                          23° C.                                                                           63 Kg · cm.sup.-2                                                                  83%       --                                            150° C.                                                                           5.8 Kg · cm.sup.-2                                                                490%       3.4 Kg · cm.sup.-2                   ______________________________________                                    

The tubing was then expanded to an internal diameter of 0.850 in. at 150° C. on a PTFE mandrel to yield heat-shrinkable tubing.

The use of a shrunk length of this tubing as a stress control covering on a high voltage cable termination will now be described with reference to FIG. 2 of the accompanying drawings which shows a sectional side elevation of one end of a 10 kilovolt cable which has been prepared for termination.

Referring to FIG. 2 of the drawings, a 10 kilovolt polyethylene cable designated generally by reference numeral 1 comprises a cenral conductor 2 surrounded by a conductive polyethylene stress control layer 3; the layer 3 being surrounded by an insulating layer 4. The bulk portion of the cable 1 also comprises a carbon paper layer 5, a copper screen 6 and an outer insulating sheath 7. The terminated portion of the cable 1 comprises the central conductor 2, the conductive polyethylene stress control layer 3, the insulating layer 4 and a short length of the carbon paper layer 5 and copper screen 6 extending from the bulk portion of the cable. The end of the cable 1 is provided with a cable lug 8 attached to the central conductor 2.

A 12 cm length of the heat-shrinkable tubing was shrunk onto the terminated portion of the cable 1 with an overlap of about 2 cm onto the extended portion of the copper screen 6, to provide a stress control covering 9. The heat-shrinkable tubing was also shrunk onto whipping 10 and an earth tail 11 within the region of overlap onto the copper screen 6. No attempt was made to fill the air gap between the covering 9 and the extended portion of the copper screen 6.

Discharge magnitude of a 2 m length of the above 10 kilovolt cable, each end of which had been terminated as described above were determined using the apparatus and circuit shown in FIG. 3 of the accompanying drawings.

Referring to FIG. 3 of the drawings, an earthed or grounded wire screen cage 12 contains a discharge-free step-up transformer 13, the secondary windings of which are connected to the central conductor 2 and the screen 6 respectively of the cable 1, through ground, via a parallel-connected voltage dropper 14 and blocking capacitor 15. The primary windings of the transformer 13 are connected to an AC input via a control and filter unit 16. Discharge levels in the cable and end terminations were measured using an ERA Mark III discharge detector 17 connected as shown.

The following results were obtained:

    ______________________________________                                         Discharge           Applied Voltage                                            Magnitude in pC     KV r.m.s.                                                  ______________________________________                                         1                   16.2                                                       5                   24.3                                                       ______________________________________                                    

For comparison, the same cable was tested without the heat-shrunk tubing or other means of stress control and the result was a discharge magnitude of 5 pC at an applied voltage of 4 KV r.m.s. Thus, it can be seen that the covering of the material of the invention affords excellent stress control and that the cable terminations are substantially discharge free at the normal working voltage of 5.8 KV (phase to ground).

EXAMPLE 2

The following substances were mixed together as described in Example 1:

    ______________________________________                                                                 Parts by                                               Substance               Weight                                                 ______________________________________                                         Royalene 512            150                                                    DPD 6169                67                                                     DYNH                    60                                                     Agerite Resin D         7.5                                                    Aerosil 200             30                                                     Silane A151             11.4                                                   SiC as in Example 1     570                                                    Zinc Stearate           10                                                     Triallyl Cyanurate      3                                                      2,5-di-methyl-2,5-di-t-butyl-                                                  peroxy-hexyne-3         2                                                      ______________________________________                                    

The nonlinear resistance behaviour of the material was determined as described in Example 1. The value of γ over the voltage range of 100 V to 10 KV was found to be 5.3.

The resulting material was pressed into test plaques of dimensions 5 in.×5 in.×0.075 in. at 190° C. for 12 minutes and the following physical properties were determined:

    ______________________________________                                                   Tensile     Elongation 100%                                          Temperature                                                                              Strength    at Break   Modulus                                       ______________________________________                                          23° C.                                                                           64 Kg . cm.sup.-2                                                                          193%       --                                            150° C.                                                                           22 Kg . cm.sup.-2                                                                          269%       14.4 Kg . cm.sup.-2                           ______________________________________                                    

Raychem cones (part no. 200 W 057 comprising a moulded tube 91/2 in. in length the wall thickness of which uniformly tapers from 0.25 in. at one end to 0.02 in. at the other end) were prepared from the material by curing in a press at 200° C. for 12 minutes. These cones were expanded to an internal diameter of 1.30 ins. by heating them to 150° C. and pushing them over a PTFE mandrel. Two of these cones were heat-shrunk onto the ends of a 20 KV cable (i.e., a cable having a working voltage of 11.6 KV phase to ground) terminated as described in Example 1; again no precautions being taken to fill the air gap. The internal diameter of the shrunk parts was 0.75 in. The discharge magnitudes were determined as described in Example 1 and the following results were obtained:

    ______________________________________                                         Discharge           Applied Voltage                                            Magnitude in pC     KV r.m.s.                                                  ______________________________________                                         1                   30                                                         5                   50                                                         Control (no stress                                                             control layer) 5    4.6                                                        ______________________________________                                    

Thus, it can be seen that the terminations are substantially discharge free at an applied voltage level of more than 2.5 times the working voltage of the cable and that the level for a discharge magnitude of 5 pC, which is normally regarded as acceptable, is nearly 5 times the working voltage.

EXAMPLE 3

To show the effect of varying ethylene content of the rubber on the physical properties of the material of the invention.

The following substances were mixed together as described in Example 1.

    ______________________________________                                                                  Parts by                                              Substance                Weight                                                ______________________________________                                         EPDM Rubber (see below)  100                                                   DYNH                     40                                                    DPD 6169                 45                                                    Agerite Resin D          5                                                     Zinc Stearate            1.8                                                   Silicon Carbide as in Example 1                                                                         380                                                   Triallyl Cyanurate       2.5                                                   ______________________________________                                    

Six different materials (A to F) were prepared, having different EPDM contents as follows:

    ______________________________________                                         Material                                                                              Parts by Weight and Nature of EPDM Rubber                               ______________________________________                                         A      100 pts  Royalene 611                                                   B      67 pts   Royalene 611                                                                              33 pts Royalene 301T                                C      33 pts   Royalene 611                                                                              67 pts Royalene 301T                                D      20 pts   Royalene 611                                                                              80 pts Royalene 301T                                E      10 pts   Royalene 611                                                                              90 pts Royalene 301T                                F                          100 pts                                                                               Royalene 301T                                ______________________________________                                    

Each material was extruded into tubing of 0.125 in. internal diameter and having a wall thickness of 0.025 in. The tubing was irradiated with γ-rays from a Co⁶⁰ source at 1.25 MeV to a dose of 12.5 Mrads after which the following properties were determined:

    ______________________________________                                                                   Elongation at                                        Material  Tensile Strength                                                                               Break (23° C.)                                ______________________________________                                         A         63 Kg · cm.sup.-2                                                                     83%                                                  B         54 Kg · cm.sup.-2                                                                     73%                                                  C         51 Kg · cm.sup.-2                                                                     62%                                                  D         54 Kg · cm.sup.-2                                                                     33%                                                  E         51 Kg · cm.sup.-2                                                                     33%                                                  F         63 Kg · cm.sup.-2                                                                     33%                                                  ______________________________________                                    

EXAMPLE 4

Use of a combination of SiC and Conducting Carbon Black.

The following substances were mixed together as described in Example 1:

    ______________________________________                                                   Material A                                                                              Material B Material C                                       ______________________________________                                         Royalene 611                                                                               100        100        100                                          DYNH        40         40         40                                           DPD 6169    45         45         45                                           Agerite Resin D                                                                            5          5          5                                            Emulsifiable                                                                   Polyethylene                                                                               5          5          5                                            Vulcan 3    --         --         8.25                                         Vulcan XXX Sp.                                                                             --         27.5       30                                           Silicon Carbide                                                                as in Example 1                                                                            380        260        200                                          Triallyl                                                                       Cyanurate   2.5        2.5        2.5                                          2,5-di-methyl-2,                                                               5-di-t-butyl-peroxy-                                                           hexyne-3    5          5          5                                            ______________________________________                                    

Plaques 1 mm. thick were moulded from each of the three materials and the electrical resistance characteristics determined as described in Example 1.

None of the materials obeyed Ohm's Law, the values of γ being:

    ______________________________________                                         Material A         5.0                                                         Material B         4.3                                                         Material C         4.4                                                         ______________________________________                                    

The current passed by the plaques at a voltage stress of 1 KV/mm was:

    ______________________________________                                         Material A        0.01 μA                                                   Material B        0.08 μA                                                   Material C        0.17 μA                                                   ______________________________________                                    

Thus, even on substantially reducing the amount of the nonlinear filler, no marked deterioration in electrical properties occurs.

Similar plaques 1 mm thick were moulded from each material and the physical properties determined at 23° C. and 150° C.

    ______________________________________                                         At                                                                             Room Temperature                                                                               At 150° C.                                              Ma-  Tensile   Elonga-  Tensile Elonga-                                                                               100%                                    ter- Strength  tion at  Strength                                                                               tion at                                                                               Modulus                                 ial  Kg · cm.sup.-2                                                                  Break %  Kg · cm.sup.-2                                                                Break %                                                                               Kg · cm.sup.-2                 ______________________________________                                         A    72.75     177      9.82    428    5.33                                    B    70.52     318      15.06   324    8.25                                    C    100.85    480      18.84   483    6.81                                    ______________________________________                                    

Two Raychem Part RUK 453-3 (a tube 100 mm long with a 3 mm wall thickness and an internal diameter of 20 mm) were moulded from Material C. These were mechanically expanded on a PTFE mandrel to an internal diameter of 40 mm. One of these tubes was shrunk on each end of a 2 m. length of Polyethylene insulated 11.6/20 KV cable, prepared for termination as described in Example 1, in such a manner that each tube overlapped the conducting screen by 20 mm.

The cable was connected to the H/V output of a 50 KV Discharge Free transformer. The discharge inception levels were measured as described in Example 1 and were found to be as follows:

    ______________________________________                                         Discharge        Applied Voltage                                               Magnitude (pC)   (KV r.m.s.)                                                   ______________________________________                                         1                26                                                            5                29                                                            ______________________________________                                    

For comparison, the same length of cable with no form of stress control gave a discharge level of 5 pC at 4.8 KV r.m.s. applied voltage.

From the foregoing results, it will be substantially seen that this material gives good stress relief; the cable being substantially discharge free at the working voltage (11.6 KV phase to ground). Further, a marked improvement in physical properties compared to articles of a material not containing a conducting particulate filler is evident.

EXAMPLES 5 TO 10

These Examples show the use of conducting particulate materials, i.e., metal powders in conjunction with silicon carbide.

    ______________________________________                                                     Example Nos.                                                       Substance     5      6      7    8    9    10                                  ______________________________________                                         Royalene 611  60     60     60   60   60   60                                  DYNH          16     16     16   16   16   16                                  DPD 6169      24     24     24   24   24   24                                  Agerite Resin D                                                                              4      4      4    4    4    4                                   Silicon Carbide                                                                (Grade F1200/3)                                                                              300    225    200  200  200  200                                 Copper Powder --     --     50   100  --   --                                  Aluminium Dust                                                                               --     75     --   --   --   --                                  Iron Powder   --     --     --   --   50   100                                 Zinc Stearate 4      4      4    4    4    4                                   Triallyl Cyanurate                                                                           1.4    1.4    1.4  1.4  1.4  1.4                                 2,5-di-methyl-2,                                                               5-di-t-butyl-                                                                  peroxy-hexyne-3                                                                              1.5    1.5    1.5  1.5  1.5  1.5                                 ______________________________________                                    

The above substances were processed as described in Example 1. The γ coefficient was measured for each material by the method described in Example 1. The values obtained were as follows:

Material of:

    ______________________________________                                         Example 1        γ.sub.1 = 2.7; γ.sub.2 = 4.0                      Example 2        5.71                                                          Example 3        γ.sub.1 = 5.0; γ.sub.2 = 3.8                      Example 4        γ.sub.1 = 5.2; γ.sub.2 = 3.7                      Example 5        4.3                                                           Example 6        7.5                                                           ______________________________________                                    

Where different slopes of the current versus stress curve were obtained for a given material, these are given as γ₁ and γ₂.

The aluminium dust was Grade 300 dust from Alcan Ltd.

The iron and copper powders were finer than 300 mesh (B.S.) and were obtained from Hopkin and Williams Ltd.

The current-voltage stress plots are shown in FIGS. 4 to 6 of the accompanying drawings.

The physical properties of the materials of Examples 5 and 6 were as follows:

    ______________________________________                                         Example Nos.           5       6                                               ______________________________________                                          23° C.                                                                        Tensile Strength Kg · cm.sup.-2                                                           52.4    35.2                                               % Elongation at Break                                                                              20      90                                          150° C.                                                                        Tensile Strength Kg · -2                                                                  7.02    5.1                                                % Elongation at Break                                                                              80      147                                                100% Modulus        --      5.1                                         ______________________________________                                    

Thus, the physical properties of the material of Example 6, containing the aluminium dust, are much better than those of Example 5 in respect of elongation at break. This difference is particularly significant at elevated temperatures.

EXAMPLE 11

This Example shows the use of a nitrile rubber.

    ______________________________________                                         Substance               7                                                      ______________________________________                                         Breon 1041              100                                                    DYNH                    50                                                     Agerite Resin D         5                                                      Silicon Carbide (Grade F1200/3)                                                                        300                                                    Triallyl Cyanurate      3                                                      2,5-di-methyl-2,                                                               5-di-t-butyl-peroxy-hexyne-3                                                                           5                                                      Zinc Stearate           3                                                      ______________________________________                                    

The above substances were processed by compounding on a twin roll laboratory mill and then pressed into plaques 6×6×0.040 ins. at 190° C. for 10 mins. The physical properties of the resulting material were as follows:

    ______________________________________                                                          23° C.                                                                           150° C.                                       ______________________________________                                         Tensile Strength Kg · cm.sup.-2                                                           49        16                                               % Elongation at Break                                                                             244        104                                              100% Modulus       --         15                                               ______________________________________                                    

The electrical properties were measured as described in Example 1 and the current-voltage stress plot revealed two γ coefficients, γ₁ =1.25 γ₂ =3.54, as shown in FIG. 7 of the accompanying drawings.

While embodiments and applications of this invention have been shown and described, it will be apparent to those skilled in the art that many more modifications are possible without departing from the inventive concepts herein described. The invention, therefore, is not to be restricted, except as is necessary by the prior art and the spirit of the appended claims. 

What is claimed as new and desired to be secured by Letters Patent of the United States is:
 1. A composition of matter having nonlinear electrical resistance characteristics comprising a blend of:(a) an ethylene-propylene rubber copolymer wherein the ethylene content is at least about 65%; (b) a copolymer of ethylene and a monomer, other than propylene, copolymerisable therewith; and (c) a low density polyethylene having dispersed therein particulate silicon carbide, of particle size finer than about 300 grit.
 2. The composition of matter as in claim 1 wherein the ethylene content of component (a) is at least about 70%.
 3. The composition of matter as in claim 1 wherein the blend comprises, per 100 parts by weight of component (a), from about 25 to about 75 parts by weight of component (b) and from about 15 to about 70 parts by weight of component (c).
 4. The composition of matter as in claim 3 wherein the blend comprises, per 100 parts by weight of component (a), from about 25 to about 50 parts by weight of component (b) and from about 20 to about 50 parts by weight of component (c).
 5. The composition of matter as in claim 1 wherein said ethylene-propylene rubber copolymer is a non-conjugated diene rubber terpolymer.
 6. The composition of matter as in claim 1 wherein said copolymerisable monomer is selected from the group consisting of methyl, ethyl and other lower alkylacrylates and -methacrylates, vinyl acetate and lower alkyl esters of maleic, fumaric and itaconic acids.
 7. The composition of matter as in claim 1 wherein component (a) contains up to about 40% by weight of a naphthenic oil processing aid.
 8. The composition of matter as claimed in claim 1 wherein, as component (b), there is used an ethylene-ethyl acrylate copolymer containing about 18% by weight of units derived from ethyl acrylate.
 9. The composition of matter as in claim 1 wherein the particulate silicon carbide has a particle size finer than about 500 grit size.
 10. The composition of matter as in claim 1 which contains from about 35 to about 45 volume % of silicon carbide based on the polymer blend.
 11. The composition of matter as in claim 1 further including a particulate electrically conductive, filler.
 12. The composition of matter as in claim 11 wherein said filler is a carbon black.
 13. The composition of matter as in claim 11 wherein said filler is a finely divided metal.
 14. A composition of matter as claimed in claim 13 wherein said metal is chosen from the group consisting of zinc, aluminum, chromium, copper, bronze, brass, iron, lead, silver and nickel.
 15. A composition of matter having non-linear electrical resistance characteristics comprising the blend of:a butadiene/acrylonitrile rubber containing from about 10% to about 40% by weight acrylonitrile; and a low density polyethylene having dispersed therein particulate silicon carbide, of particle size finer than about 300 grit.
 16. The composition of matter as in claim 1 wherein the particle size of component (c) is finer than about 400 grit.
 17. A composition of matter having nonlinear electrical resistance characteristics comprising a blend of:a. a butadiene/acrytronitrile rubber containing from about 10 percent to about 40 percent by weight acrytronitrile; b. a copolymer of ethylene and a monomer other than propylene copolymerisable therewith; and c. A low density polyethylene having dispersed therein particulate silicon carbide of particle size finer than about 300 grit.
 18. The composition of matter as in claim 17 wherein said copolymerisable monomer is selected from the group consisting of methyl, ethyl and other lower alkylacrylates and -methacrylates, vinyl acetate and lower alkyl esters of maleic, fumaric and itaconic acids.
 19. The composition of matter as in claim 17 wherein the copolymer of ethylene and a monomer copolymerisable therewith comprises an ethylene-ethyl acrylate copolymer comprising about 18 percent by weight of units derived from ethyl acrylate.
 20. The composition of matter as in claim 17 wherein the particulate silicon carbide has a particle size finer than about 500 grit size.
 21. The composition of matter as in claim 17 which contains from about 35 to 45 volume percent of silicon carbide based on the polymer blend.
 22. The composition of matter as in claim 17 further including a particulate electrically conductive filler.
 23. The composition of matter as in claim 22 wherein said filler is a carbon black.
 24. The composition of matter as in claim 22 wherein said filler is a finely divided metal.
 25. A composition of matter as in claim 24 wherein said metal is chosen from the group consisting of zinc, aluminum, chromium, copper, bronze, brass, iron, lead, silver and nickel. 